Mössbauer characterization of iron oxide nanoclusters grown within aluminosilicate matrices

Georgia C. Papaefthymiou, A. Bustamante Dominguez, Rosa B. Scorzelli

Research output: Contribution to conferencePaper

1 Scopus citations


Mössbauer spectroscopy uses the resonant absorption of nuclear radiation by 57Fe to probe the electronic and internal magnetic structure of iron based magnetic materials. The technique has a characteristic measuring time of 10 ns enabling investigation of spin relaxation phenomena in nanoscale particles; and determination of their magnetic properties in the absence of externally applied magnetic fields. We report on Mössbauer studies of γ-Fe2O3 nanoparticles synthesized within hexagonally packed mesoporous MCM-41 aluminosilicate matrices with cylindrical pores of 2.5 nm diameter. Data analysis allowed differentiation of particle-matrix interfacial versus particle-core interior iron sites. Interfacial iron atoms experience large electric field gradients resulting in quadrupole splitting values of ΔEq (surface) = (1.25 ± 0.05) mm/s, while core atoms exhibit smaller values of ΔEq (core) = (0.73 ± 0.05) mm/s at room temperature. Similarly, differences were observed in the values of the internal hyperfine fields at low temperatures indicating reduced strength in the exchange interactions at the particle surface, with interfacial atoms experiencing internal fields Hhf (surface) = (458 ± 1) kOe reduced relative to the core Hhf (core) = (488 ± 1) kOe at 4.2 K. Particle/matrix interactions at the surface appear to perturb the electronic interactions deeper into the core than the magnetic exchange interactions.
Original languageAmerican English
Number of pages6
StatePublished - 1 Dec 2002
EventMaterials Research Society Symposium - Proceedings -
Duration: 1 Dec 2002 → …


ConferenceMaterials Research Society Symposium - Proceedings
Period1/12/02 → …


Dive into the research topics of 'Mössbauer characterization of iron oxide nanoclusters grown within aluminosilicate matrices'. Together they form a unique fingerprint.

Cite this