The role of Fe-doping on structural and magnetic properties of Fe nanoclusters in thick Yb films

C. Rojas-Ayala, E. C. Passamani, M. A. Sousa, F. J. Litterst, E. M. Baggio-Saitovitch

Research output: Contribution to journalArticlepeer-review

1 Scopus citations


© 2016 Elsevier B.V. All rights reserved. Structural and magnetic properties of co-deposited (x at.% Fe)Yb (0.3≤x≤5.0) films have systematically been investigated by X-ray absorption spectroscopy, 57Fe Mössbauer spectroscopy, magnetization measurements, and Ferromagnetic Resonance (FMR) experiments. Mössbauer and magnetization data indicate formation of two types of Fe clusters that are supposed to be at grain boundaries in fcc- and hcp-like Yb structures. Clusters stay superparamagnetic down to 3 K for low Fe concentrations x. For the highest studied Fe concentration x=5.0 we find blocking behavior typical for only very weakly interacting cluster magnetic moments with blocking temperature of ca. 7 K. EXAFS can only resolve one type of Fe-Fe and one of Fe-Yb nearest neighbor coordination, both with a lack of long-range structural order. While the coordination number of Fe increases and that of Yb decreases with increasing Fe concentration (as expected for a growing size of Fe clusters), the nearest neighbor distances remain practically unchanged for different Fe content. Estimated cluster sizes are on the order of nm. FMR experiments suggest that the average ratio of orbital to spin magnetic moment of Fe in (x at.% Fe)Yb films decreases with increasing x thus indicating the decreasing contribution from the fraction of Fe atoms on the cluster surfaces.
Original languageAmerican English
Pages (from-to)175-181
Number of pages7
JournalJournal of Magnetism and Magnetic Materials
StatePublished - 1 Nov 2016


Dive into the research topics of 'The role of Fe-doping on structural and magnetic properties of Fe nanoclusters in thick Yb films'. Together they form a unique fingerprint.

Cite this