Mössbauer study of the nanocrystallization of the amorphous system Fe73.5Si13.5B9Cu1Nb 1X2 with X = Nb, Mo, V and Zr

J. M. Borrego, V. A.Peña Rodríguez, A. Conde

Resultado de la investigación: Contribución a una revistaArtículorevisión exhaustiva

1 Cita (Scopus)

Resumen

Amorphous to crystalline transformation after isochronal annealing of as-quenched ribbons with the composition Fe73.5Cu1Nb1Si13.5B 9X2 (X = Zr, Nb, Mo, V) was investigated by the combined use of differential scanning calorimetry and Mössbauer spectroscopy. Alloying raises the thermal stability in the order V < Mo < Nb < Zr. The fraction of the Mössbauer subspectra corresponding to the nanophase for the same annealing conditions decreases in the order V > Mo > Nb > Zr.

Idioma originalInglés
Páginas (desde-hasta)1-6
Número de páginas6
PublicaciónHyperfine Interactions
Volumen110
N.º1-2
EstadoPublicada - 1997

Huella

Profundice en los temas de investigación de 'Mössbauer study of the nanocrystallization of the amorphous system Fe<sub>73.5</sub>Si<sub>13.5</sub>B<sub>9</sub>Cu<sub>1</sub>Nb <sub>1</sub>X<sub>2</sub> with X = Nb, Mo, V and Zr'. En conjunto forman una huella única.

Citar esto