Understanding the electronic properties of BaTiO<inf>3</inf>and Er<sup>3+</sup>doped BaTiO<inf>3</inf>films through confocal scanning microscopy and XPS: The role of oxygen vacancies

J. L. Clabel H., Iram T. Awan, G. Lozano, M. A. Pereira-Da-Silva, R. A. Romano, V. A.G. Rivera, S. O. Ferreira, E. Marega

Resultado de la investigación: Contribución a una revistaArtículorevisión exhaustiva

1 Cita (Scopus)

Resumen

© the Owner Societies. Photonic and electronic properties exist inherently in ferroelectric barium titanate (BaTiO3); severe luminescence quenching also exists due to the insufficient confinement of excitons. In this sense, high optical emission can only be achieved by its chemical and structural modification. Thin BaTiO3 and Er:BaTiO3 films were grown by the spin coating method on a glass substrate at room temperature. Self-trapping of excitons in the thin BaTiO3 film and its structural modification due to the doping with Er3+ ions (Er:BaTiO3) are verified using scanning confocal fluorescence microscopy (SCFM), where self-trapping excitons never occured in its pure state. By thermal treatment and doping (BaTiO3 and Er:BaTiO3) we obtained localization of the excitons, which would further induce lattice strain around the surface defects, to accommodate the self-trapped excitons. With such a self-trapped state, the structure of BaTiO3 generates broadband emission of several overlapping bands between 1.95 and 2.65 eV at room temperature, while the structure Er:BaTiO3 showed defined emission bands at 2.24 and 2.35 eV, with very weak contributions of the emission due to the self-trapping state. The influence of the variation of the excitation wavelength using 1PE and 2PE on the emission bands of BaTiO3 and Er:BaTiO3 is also investigated. The results of enhanced emission bands suggest a clear dependence of the emission intensity on the excitation energy, where a ∼3 fold enhancement in emission has been demonstrated under Er3+ (1.55 eV) excitation, which can be attributed to effective energy transfer between the Er3+ ions. As a result, it is concluded that the developed BaTiO3 and Er:BaTiO3 can pave the way for future photonic devices.
Idioma originalInglés estadounidense
Páginas (desde-hasta)15022-15034
Número de páginas13
PublicaciónPhysical Chemistry Chemical Physics
DOI
EstadoPublicada - 14 jul 2020

Huella Profundice en los temas de investigación de 'Understanding the electronic properties of BaTiO<inf>3</inf>and Er<sup>3+</sup>doped BaTiO<inf>3</inf>films through confocal scanning microscopy and XPS: The role of oxygen vacancies'. En conjunto forman una huella única.