TY - JOUR
T1 - Vacancy ordered γ-Fe 2 O 3 nanoparticles functionalized with nanohydroxyapatite: XRD, FTIR, TEM, XPS and Mössbauer studies
AU - Ramos Guivar, Juan A.
AU - Sanches, Edgar A.
AU - Bruns, Florian
AU - Sadrollahi, Elaheh
AU - Morales, M. A.
AU - López, Elvis O.
AU - Litterst, F. Jochen
PY - 2016/12/15
Y1 - 2016/12/15
N2 - © 2016 Elsevier B.V. Vacancy ordered maghemite (γ-Fe 2 O 3 ) nanoparticles functionalized with nanohydroxyapatite (HAp – Ca 10 (PO 4 ) 6 (OH) 2 ) have been successfully synthesized using an inexpensive co-precipitation chemical route. Evidence for the presence of vacancy order in maghemite was shown by the superstructure lines observed in X-ray diffraction. The adsorption of carboxyl groups of citric acid (C 6 H 8 O 7 ) onto γ-Fe 2 O 3 nanoparticles was investigated by FTIR, XPS and Mössbauer spectroscopy. From XPS surface analysis, two binding energies related to oxygen were attributed to bindings between C 6 H 8 O 7 /γ- Fe 2 O 3 and C 6 H 8 O 7 /HAp from an interfacial reaction promoted by strongly adsorbed H 2 O molecules at the surface of these nanomaterials. Le Bail refinement of the XRD patterns showed the formation of well-crystallized pure tetragonal maghemite before and after functionalization with nanoHAp. The temperature dependence of hyperfine parameters of pure and functionalized γ-Fe 2 O 3 nanoparticles was investigated via Mössbauer spectroscopy. TEM revealed the formation of quasi-spherical γ- Fe 2 O 3 nanoparticles with an average diameter of ca. 12 nm and 16 nm before and after functionalization with nanoHAp in agreement with Le Bail refinement. Magnetometry measurements showed a saturation magnetization of 12 emu/g and a blocking temperature of 340 K for the functionalized γ- Fe 2 O 3 nanoparticles.
AB - © 2016 Elsevier B.V. Vacancy ordered maghemite (γ-Fe 2 O 3 ) nanoparticles functionalized with nanohydroxyapatite (HAp – Ca 10 (PO 4 ) 6 (OH) 2 ) have been successfully synthesized using an inexpensive co-precipitation chemical route. Evidence for the presence of vacancy order in maghemite was shown by the superstructure lines observed in X-ray diffraction. The adsorption of carboxyl groups of citric acid (C 6 H 8 O 7 ) onto γ-Fe 2 O 3 nanoparticles was investigated by FTIR, XPS and Mössbauer spectroscopy. From XPS surface analysis, two binding energies related to oxygen were attributed to bindings between C 6 H 8 O 7 /γ- Fe 2 O 3 and C 6 H 8 O 7 /HAp from an interfacial reaction promoted by strongly adsorbed H 2 O molecules at the surface of these nanomaterials. Le Bail refinement of the XRD patterns showed the formation of well-crystallized pure tetragonal maghemite before and after functionalization with nanoHAp. The temperature dependence of hyperfine parameters of pure and functionalized γ-Fe 2 O 3 nanoparticles was investigated via Mössbauer spectroscopy. TEM revealed the formation of quasi-spherical γ- Fe 2 O 3 nanoparticles with an average diameter of ca. 12 nm and 16 nm before and after functionalization with nanoHAp in agreement with Le Bail refinement. Magnetometry measurements showed a saturation magnetization of 12 emu/g and a blocking temperature of 340 K for the functionalized γ- Fe 2 O 3 nanoparticles.
UR - https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=84982803951&origin=inward
UR - https://www.scopus.com/inward/citedby.uri?partnerID=HzOxMe3b&scp=84982803951&origin=inward
U2 - 10.1016/j.apsusc.2016.07.157
DO - 10.1016/j.apsusc.2016.07.157
M3 - Article
SN - 0169-4332
SP - 721
EP - 734
JO - Applied Surface Science
JF - Applied Surface Science
ER -